== Information on the origin and formation of thenardite / mirabilite in monuments  ==
== Information on the origin and formation of thenardite / mirabilite in monuments  ==


With the entry of materials that contain soluble sodium compounds, the mineral system of a monument may create sodium sulfate as salt efflorescence, when reacting with various sources of sulfate for example air contaminated with sulphurous gases. In Germany cement exhibits a high content of sodium ions, because the German standardization institute (DIN) allows for a content of up to 0.5 %  soluble alkalis. This means that 100 kg of Portland cement containing only 0.1% soluble Na<sub>2</sub>O can form 520g of [[Mirabilite]] when in contact with air containing sulfuric acid [calculation by Arnold/Zehnder 1991]. Sodium ions can also enter into monuments from a plethora of cleaning materials and especially older restoration products (such as water glass). Ground water and surface water are also a possible source of Na<sup>+</sup>-ions. Road salt consists to a large extent of slightly soluble [[Halite|sodium chloride]]. Finally, in the coastal areas, sea water is a significant source of [[Halite|NaCl]].
With the entry of materials that contain soluble sodium compounds, the mineral system of a monument may create sodium sulfate as salt efflorescence, when reacting with various sources of sulfate for example air contaminated with sulphurous gases. In Germany cement exhibits a high content of sodium ions, because the German standardization institute (DIN) allows for a content of up to 0.5 %  soluble alkalis. This means that 100 kg of Portland cement containing only 0.1% soluble Na<sub>2</sub>O can form 520g of [[Mirabilite]] when in contact with air containing sulfuric acid [calculation by Arnold/Zehnder 1991]. Sodium ions can also enter into monuments from a plethora of cleaning materials and especially older restoration products (such as water glass). Ground water and surface water are also a possible source of Na<sup>+</sup>-ions. Road salt consists to a large extent of slightly soluble [[Halite|sodium chloride]]. Finally, in coastal areas, sea water is a significant source of [[Halite|NaCl]].


== Solubility behavior  ==
== Solubility behavior  ==

Revision as of 13:54, 6 May 2012

Thenardite[1][2]
HJS-Na2SO4-111703-02-10x.jpg
Mineralogical name Thenardite
Chemical name Sodium sulfate
Trivial name Pyrotechnite
Chemical formula Na2SO4
Other forms Mirabilite (Na2SO4•10H2O)
Sodiumsulfate heptahydrate (Na2SO4•7H2O)
Crystal system orthorhombic
Crystal structure
Deliquescence humidity 20°C 81.7% (25°C)
Solubility (g/l) at 20°C 162 g/l
Density (g/cm³) 2.689 g/cm³
Molar volume 53.11 cm3/mol
Molar weight 142.04 g/mol
Transparency transparent to translucent
Cleavage perfect
Crystal habit
Twinning
Phase transition
Chemical behavior
Comments soluble in water and glycerin,
not soluble in pure alcohol
Crystal Optics
Refractive Indices nx = 1.468
ny = 1.473
nz = 1.483
Birefringence Δ = 0.015
Optical Orientation positive
Pleochroism
Dispersion
Used Literature
{{{Literature}}}


Authors: Hans-Jürgen Schwarz , Michael Steiger, Tim Müller
English translation by Matthieu Angeli
back to Sulfate

Sodium sulfate and thenardite[edit]

Abstract[edit]

Sodium sulfate and its phases thenardite, mirabilite and heptahydrate are described. Heptahydrate´s role as a major source of damage is also explained .

Occurrence[edit]

Both thenardite and mirabilite occur as natural minerals. In nature sodium sulfate occurs in mineral waters in the form of double salts, as deposits of former salt lakes. Knowledge of the hydrated sodium sulfate dates back to the 16th Century. Its first description has been written by Glauber in 1658 in which he described it as "sal mirable". It is also quite common to read the name "Glauber's salt" for mirabilite in the literature.

Information on the origin and formation of thenardite / mirabilite in monuments[edit]

With the entry of materials that contain soluble sodium compounds, the mineral system of a monument may create sodium sulfate as salt efflorescence, when reacting with various sources of sulfate for example air contaminated with sulphurous gases. In Germany cement exhibits a high content of sodium ions, because the German standardization institute (DIN) allows for a content of up to 0.5 % soluble alkalis. This means that 100 kg of Portland cement containing only 0.1% soluble Na2O can form 520g of Mirabilite when in contact with air containing sulfuric acid [calculation by Arnold/Zehnder 1991]. Sodium ions can also enter into monuments from a plethora of cleaning materials and especially older restoration products (such as water glass). Ground water and surface water are also a possible source of Na+-ions. Road salt consists to a large extent of slightly soluble sodium chloride. Finally, in coastal areas, sea water is a significant source of NaCl.

Solubility behavior[edit]

Figure1: Solubility of Na2SO4 in water, Graph: M. Steiger


The structures of both thenardite and mirabilite belong to the group of easily soluble salts and therefore they are easily mobilized (see table hygroscopicity of the salts and ERH). The solubility of sodium sulfate is highly dependent on temperature. For this reason, a rapid drop of temperature is highly likely to yield very high supersaturation and salt crystallization.

Hygroscopicity[edit]

Figure2:Deliquescence of Na2SO4, Graph: M. Steiger

The temperature effect on the deliquescence points of thenardite and mirabilite is shown below. The striking features here are the opposite curve transitions. In the presence of other ions (in salt mixtures), the parameters of the equilibrium moisture content, as well as the necessary temperature and humidity conditions for recrystallization, change significantly. The following table shows experimental data of equilibrium moisture for different salt mixtures at different temperatures.It turns out that all the values of equilibrium moisture content are lower than those of the pure salt mirabilite (see table equilibrium moisture content as a function of temperature).


Table 1 - Information about the equilibrium moisture of saturated solid solutions (mixing ratio: saturated sol.A / saturated sol.B = 1:1) [Vogt.etal:1993]Title: Der Einfluss hygroskopischer Salze auf die Gleichgewichtsfeuchte und Trocknung anorganischer Baustoffe
Author: Vogt, R.; Goretzki, Lothar
Link to Google Scholar
MgSO4 Ca(NO3)2 KNO3
Na2SO4 • 10H2O 87(21°C) 74 (21°C) 81(21°C)


Water vapor sorption:

Figure 3: Deliquescence points of pure salts thenardite and mirabilite [Arnold.etal:1991]Title: Monitoring Wall Paintings Affected by soluble Salts
Author: Arnold, Andreas; Zehnder, Konrad
Link to Google Scholar

The table below shows additional information for estimating the hygroscopicity of sodium sulfate for the sorption behavior of pure salt and the mixture with halite at different relative humidity levels:


Table 2: Moist sorption of sodium sulphate in M.% after 56 days of storage [after [Vogt.etal:1993]Title: Der Einfluss hygroskopischer Salze auf die Gleichgewichtsfeuchte und Trocknung anorganischer Baustoffe
Author: Vogt, R.; Goretzki, Lothar
Link to Google Scholar
]
Air humidity 87% r.F. 81% r.F. 79% r.F.
Na2SO4 79 0 0
Na2SO4+NaCl (1:1 molar mixture) 157 32 15

Crystallization pressure[edit]

When crystallizing from an aqueous solution, the crystallization pressure of thenardite lies in the 29.2-34.5 N/mm2 range. These values are higher that those calculated for other building-damaging salts [Winkler:1975]Title: Stone: Properties, Durability in Man´s Environment
Author: Winkler, Erhard M.
Link to Google Scholar
.

Hydration behavior[edit]

Error creating thumbnail:
Conversion of mirabilite (?) into thenardite

The Na2SO4 – H2O system:

The only stable forms of sodium sulfate are the decahydrate (mirabilite) and the anhydrite (thenardite). The generation of mirabilite by recrystallization of the salt from an aqueous supersaturated solution occurs at 32.4°C. In particular, the transition from thenardite to mirabilite and the incorporation of 10 water molecules in the crystal lattice causes a volume expansion of 320%. This transition happens at a relatively low temperature (32-35°C), the damage caused by this salt is highly dependent on the temperature and thus on the environment. This temperature range is given as a guide, because this transition could happen for example at 25°C at 80% relative humidity, or even at 0°C at 60.7% relative humidity [information from Gmelin]. Due to this strong dependence on the environmental parameters, an estimate of the damage caused on buildings by crystallization and hydration of sodium sulfate are very difficult to obtain.

Pictures of salt and salt damage[edit]

In the field[edit]

Under the polarizing microscope[edit]


Weblinks
[edit]